Welding Electrode (AWS E6013 GB E4303 JIS D4303)

Welding Electrode (AWS E6013 GB E4303 JIS D4303)
Product Detailed

ABS, BV, GL
Stable electric arc
Low splashing
low price
good quality

AWS ER70S-6 BS A18 EN G3Si1

 Wire Size

 Spool Size

 Net Weight

 0.8mm
1.0mm
1.2mm
1.6mm

 D100mm D200mm
D270mm D300mm K300mm

 1kg5kg15kg18kg20kg

 

chemical composition
of welding wire(%)

C

Mn

Si

P

S

Cr

Ni

Cu

0.06~0.15

1.40~1.85

0.80~1.15

≤0.025

≤0.035

-

-

≤0.50

Mechanical Properties
or
Deposited Metal

Yield strengthσ0.2(Mpa)

Tensile strengthσb(Mpa)

Elongationδ5(%)

AKV impact(J)

≥420

≥500

≥22

≥27(-29)

 

Wire Size
(mm)

φ0.8

φ1.0

φ1.2

φ1.6

Welding position

 

Welding current(A)

40~140

50~220

80~350

120~550

Please be noted

Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.

Before welding please clean out the
oil,rust,water etc from the work parts

E6013 Welding Electrodes AWS E6013 is a low-carbon steel electrode with a high titaniume coating and can be used on A . C . or D . C . It  has excellent welding technological properties. The arc is stable .  The spatter is small. The slag viscosity is moderate. It can be used freely . The slag  is  easy to clean . The welded seam is smooth  and fine and easy to restrike the arc.Application: Suitable  for  welding  sheet  metal  structure  made  of  low-carbon  steel , such  as  ships, vehicles, building, and general machinery. Chemical Composition of Wire(%):

C

Mn

Si

S

P

≤0.12

0.3-0.6

≤0.35

≤0.035

≤0.040

Mechanical Properties of Deposited Metal:

Test Item

σb(MPa)

σc(MPa)

δs(%)

Akv(c)(J) 

Guarantee Value

≥420

≥330

≥17

-

Recommended Welding Current:

Electrode Diameter(mm)

2.0

2.5

3.2

4.0

5.0

Current Range(A)

40-70 

50-80

80-120

150-190 

180-240

 3. E7018 Welding Electrodes    Description: AWS E7018 is low-hydrogen potassium coating  carbon  steel welding  rod  and  can be  used on  A .C  or   D .C  . It  has  excellent welding  technological  properties. It can be used various composition . Its evident trait is composed of Fe power and can reduce welding layer.
Application:  Suitable for welding important structures made of low alloy steel.Chemical Composition of Wire(%):

C

Mn

Si

S

P

≤0.12

≤0.16 

≤0.75

≤0.035

≤0.040

Mechanical Properties of Deposited Metal:

Test Item

σb(MPa)

σc(MPa)

δs(%)

Akv(C)(J)

Guarantee Value

≥490

≥400

≥22

(-30C)≥27

Recommended Welding Current:

Electrode Diameter(mm)

2.0

2.5

3.2

4.0

5.0

Current Range(A)

60-90

90-120

120-150

170-200

210-250

 